500°F/260°C Continuous Exposure: Higher Intermittent
Aerospace AS1072 Grade Fire Sleeve
Aerospace AS1072 Grade Fire Sleeve was specially developed to meet the fire resistance requirements of FAATSO - C53a OR TSO - C75.
Aerospace AS1072 Grade Fire Sleeve can withstand repeated exposures to molten steel, molten aluminum and molten glass up to 3000°F (1650°C).
Sheds splash immediately
Aerospace AS1072 Grade Fire Sleeve withstands repeated exposures to molten steel, molten aluminum and molten glass up to 3000°F (1650°C). The heavy coating of our proprietary iron oxide red silicone rubber compound sheds molten metal splash immediately, so very little heat transfer occurs.
Withstands intense radiant heat and flame
Aerospace AS1072 Grade Fire Sleeve will withstand continuous exposure to 500° F (260°C); up to 2000°F (1090°C) for 15-20 minutes; and up to 3000°F (1650°C) for 15-30 seconds. When exposed to flame, the silicone rubber transforms into a crust, creating a protective SiO2 refractory layer.
Aerospace AS1072 Grade Fire Sleeve is constructed from high bulk glass fiber braided sleeve. Excellent modulus of elasticity makes it an excellent choice for bundling hoses, tubes and cables in a variety of hostile environments.
Protect your personnel and cut your energy loss
Aerospace AS1072 Grade Fire Sleeve is insulation properties provide personnel with effective protection against burns from hot hoses and flexible steam lines, while reducing heat energy losses.
Always wear safety glasses, dust mask, gloves and long sleeves are recommended when handling this product
Proudly Made By BST Thermal Protection Products Co.,Ltd
Inside diameter - mm Inside diameter tolerance - mm Thickness and tolerance - mm
4-10 ± 0.3 3.0 ± 0.2
12-18 ± 0.4 3.5 ± 0.3
20-32 ± 0.8 4.0 ± 0.4
35-55 ± 1.0 4.3 ± 0.5
60-100 ± 1.0 4.5 ± 0.5
105-150 ± 1.0 5.5 ± 0.5
Aerospace AS1072 Grade Fire Sleeve - Quick Facts
Custom colours available by special order.
Continuous operating temp:
Max short term exposure:
Molten splash resistance:
Water and oil resistance: